Raman phonons in RuSr2GdCu2O8

M. N. Iliev, A. P. Litvinchuk, V. N. Popov, R. L. Meng, L. M. Dezaneti, C. W. Chu

研究成果: Conference article同行評審

10 引文 斯高帕斯(Scopus)

摘要

The Raman spectra of polycrystalline samples of RuSr2GdCu2O8, annealed under high pressure (3 Gpa, 1000°C), were studied between 10 and 420 K. The ferromagnetic ordering has a little (if any) effect on the variations with temperature of the position and width of the Raman lines at 158, 318, 440 and 659 cm-1. In contrast, for the line near 270 cm-1 one observes a local maximum of the halfwidth near the magnetic transition and strong hardening upon cooling below Tc. The observation of the latter line, which has no analog in the YBCO-type compounds, supports either I4/mcm or P4/mbm crystal structure, where, due to the tilting of the RuO6 octahedra, the unit cell is doubled and new Raman modes are activated. The lattice dynamical calculations (LDC) predict that the Raman mode with the closest wavenumber to that of the 270 cm-1 line is the A1g mode involving rotations of CuO5 pyramids. Such an assignment alone cannot explain the anomalous behavior near Tc. A reasonable explanation could be given considering the 270 cm-1 line as a superposition of two A1g lines corresponding to rotations around c-axis of CuO5 pyramids (265 cm-1) and RuO6 octahedra (275 cm-1), respectively.

原文English
頁(從 - 到)2209-2212
頁數4
期刊Physica C: Superconductivity and its applications
341-348 (IV)
DOIs
出版狀態Published - 2000 十一月
事件International Conference on Materials and Mechanisms of Superconductivity High Temperature Superconductors VI - Houston, TX, USA
持續時間: 2000 二月 202000 二月 25

All Science Journal Classification (ASJC) codes

  • 電子、光磁材料
  • 凝聚態物理學
  • 能源工程與電力技術
  • 電氣與電子工程

指紋

深入研究「Raman phonons in RuSr<sub>2</sub>GdCu<sub>2</sub>O<sub>8</sub>」主題。共同形成了獨特的指紋。

引用此