Reaction between TiC or TiN powder and high temperature-high pressure water

Masahiro Yoshimura, Makoto Hayakawa, Shigeyuki Somiya

研究成果: Article同行評審

5 引文 斯高帕斯(Scopus)

摘要

The reactions between TiC or TiN powder and H2O have been studied at 200°-650°C under 100 MPa. The reaction of TiC with H2O above 400°C for 3 h yielded anatase, CH4, CO2 and H2, and above 500°C rutile was formed additionally. TiN power with an average grain size of 1.4 μm reacted with H2O above 290°C to yield anatase, NH3 and H2, while TiN powder of 9 μm reacted H2O above 480°C and yielded rutile, NH3 and H2. The oxidation rate calculated from the weight gain was compared with model kinetic equations. In TiC the rate was best described by the Avrami-Erofeev equation (n=1.3), while the core-shrinking model fitted as well. This suggests that the reaction was controlled by the phase boundary reactions. In TiN the Jander-type model was best, which suggests that the reaction was controlled by diffusion through the oxide scale. An Arrhenius plot of the rate constants gave an apparent activation energy of 98 kJ/mol. The difference between reaction mechanisms is attributed to the difference in the gaseous species of reaction products.

原文English
頁(從 - 到)1339-1347
頁數9
期刊Nippon Seramikkusu Kyokai Gakujutsu Ronbunshi/Journal of the Ceramic Society of Japan
97
發行號11
DOIs
出版狀態Published - 1989

All Science Journal Classification (ASJC) codes

  • 陶瓷和複合材料
  • 化學 (全部)
  • 凝聚態物理學
  • 材料化學

指紋

深入研究「Reaction between TiC or TiN powder and high temperature-high pressure water」主題。共同形成了獨特的指紋。

引用此