Reaction-induced phase separation in a semiinterpenetrating network of reactive ternary blends

研究成果: Article同行評審

7 引文 斯高帕斯(Scopus)

摘要

Morphology and reaction mechanisms were probed on a model reactive ternary blend system of polycarbonate (PC), poly(methyl methacrylate) (PMMA), and diglycidylether of bisphenol-A (DGEBA) epoxy by using differential scanning calorimetry (DSC), scanning electron microscopy (SEM), and Fourier transform infrared spectroscopy (FTIR). Molecular interactions/reactions between the components in the blends after heating treatments are discussed. It was found that reactions took place among the components and that an interpenetrating network was built. The possible reaction mechanisms and the resulting structures after the heating treatments were probed. In the blends, PC and DGEBA reacted to form a network, while PMMA remained free. The semiinterpenetration, however, did not result in a network interlocked into a homogeneous state. The single Tg of the heated ternary DGEBA/PC/PMMA blends actually did not reflect a homogeneous interpenetrating network. Due to relatively small PMMA domains, the ternary blend network exhibited a single Tg. Upon etching the PMMA domains from the blend by acetone, a clearly interpenetrating network of reacted PC and epoxy was exposed and confirmed. The reactions leading to such a morphology are discussed with experimental evidence.

原文English
頁(從 - 到)781-788
頁數8
期刊Journal of Polymer Science, Part A: Polymer Chemistry
34
發行號5
DOIs
出版狀態Published - 1996 四月 15

All Science Journal Classification (ASJC) codes

  • 聚合物和塑料
  • 有機化學
  • 材料化學

指紋

深入研究「Reaction-induced phase separation in a semiinterpenetrating network of reactive ternary blends」主題。共同形成了獨特的指紋。

引用此