Realization of fluorescence color tuning for poly(p-phenylenevinylene) coated microspheres via a heterogeneous catalytic thermal elimination process

Yun Chen, Tian Qiu, Wei Zhao, Li Juan Fan

研究成果: Article同行評審

10 引文 斯高帕斯(Scopus)

摘要

Poly(p-phenylenevinylene) (PPV) fluorescent microspheres were prepared in two steps. First, the positive sulfonium-salt PPV precursor (pre-PPV) was coated onto the surface of negatively charged polymer substrate spheres; second, the pre-PPV was converted into fluorescent PPV via a heterogeneous catalytic thermal elimination process. A series of fluorescent microspheres were obtained with different apparent colors and different fluorescence emissions simply by varying the elimination temperature. A spectroscopy study showed that, compared to the direct solid elimination, the spheres obtained via catalyzed elimination gave a very large variation in the emission, such as a larger shift in the wavelength, and more delicate spectra profiles with peaks and shoulders. Overlapping of the signals from blue channels and green channels in the confocal microscopy study gave a direct view of the gradual change from the blue emission to the green emission for the spheres obtained at elimination temperatures from 40 °C to 120 °C. Flow cytometry measurements showed that spheres obtained at different temperatures exhibit different combinations of the intensities from four different receiving channels. These PPV spheres were also demonstrated to have a smooth surface, monodispersity, a clear core-shell structure, thermal stability and photostability. This journal is

原文English
頁(從 - 到)1576-1583
頁數8
期刊Polymer Chemistry
6
發行號9
DOIs
出版狀態Published - 2015 三月 7

All Science Journal Classification (ASJC) codes

  • Bioengineering
  • Biochemistry
  • Polymers and Plastics
  • Organic Chemistry

指紋 深入研究「Realization of fluorescence color tuning for poly(p-phenylenevinylene) coated microspheres via a heterogeneous catalytic thermal elimination process」主題。共同形成了獨特的指紋。

引用此