Recovery Zinc and Manganese from Spent Battery Powder by Hydrometallurgical Route

Wei Sheng Chen, Chin Ting Liao, Kuan Yan Lin

研究成果: Conference article同行評審

24 引文 斯高帕斯(Scopus)

摘要

Spent Zn-MnO2 battery electrode powder, containing 30.1% of Mn and 25.6% Zn was was treated via reductive leaching by H2SO4 and selective precipitation by NaOH at pH 13 for Mn(OH)2 and then pH 10 for Zn(OH)2, and the hydroxides converted respectively to MnO2 and ZnO by calcination. The effects of H2SO4 concentration, leaching time, solid-liquid ratio, reaction temperature were investigated. H2SO4 can totally dissolve Zn, but leaching rate of manganese is only 60% because of the existence of Mn (IV). Ascorbic, citric and oxalic acids were tested as the reducing agent, and ascorbic acid performs the better efficiency. The optimal reductive leaching condition were determined as 0.5 mol/L of H2SO4, 20 ml/g, 25°C, ascorbic acid dosage 10g/L for 2hours. Yielding up to 98% leaching efficiency of the two metals. The recovery rates are about 91% for Zn and 94% for Mn with high purity.

原文English
頁(從 - 到)167-174
頁數8
期刊Energy Procedia
107
DOIs
出版狀態Published - 2017 二月 1
事件3rd International Conference on Energy and Environment Research, ICEER 2016 - Barcelona, Spain
持續時間: 2016 九月 72016 九月 11

All Science Journal Classification (ASJC) codes

  • 能源(全部)

指紋

深入研究「Recovery Zinc and Manganese from Spent Battery Powder by Hydrometallurgical Route」主題。共同形成了獨特的指紋。

引用此