Reliability analysis of a bulk carrier with the combined effects of corrosion and fatigue cracks

Joe-Ming Yang, Y. J. Xu

研究成果: Article同行評審

摘要

Generally, the structures of large ships are made of steel, The corrosion and fatigue of the steel may occur due to fluctuating waves and harsh environment. The purpose of this study is to assess the reliability of a ship under extreme loading condition and severe environment. The process of corrosion may be separated into two stages. The first phase is the time period in which the corrosion protection is effective, and corrosion does not occur. The second one starts when the effectiveness of the coating is lost, and general corrosion is developing. Fatigue and corrosion are inevitable in sea-going ships and offshore structures. In order to obtain the accurate reliability of a ship's hull, one should take account of the combined effects of fatigue and corrosion. Both coating life and the time it takes to have a crack initiation are considered as random variables in this study. In the fatigue analysis of a ship's hull, two stages are also investigated. First of all. the reliability is evaluated before the crack initiation. Afterwards, the reliability after crack initiation is also calculated. Finally, based on the combined effects of fatigue and corrosion, the reliability or the probability of failure of a bulk carrier is studied.

原文English
頁(從 - 到)59-70
頁數12
期刊Journal of Taiwan Society of Naval Architects and Marine Engineers
29
發行號2
出版狀態Published - 2010 五月 1

All Science Journal Classification (ASJC) codes

  • 海洋工程
  • 機械工業

指紋

深入研究「Reliability analysis of a bulk carrier with the combined effects of corrosion and fatigue cracks」主題。共同形成了獨特的指紋。

引用此