Sb doping effects on the piezoelectric and ferroelectric characteristics of lead-free Na0.5K0.5Nb1-x SbxO 3 piezoelectric ceramics

I. Hao Chan, Chieh Tze Sun, Mau Phon Houng, Sheng Yuan Chu

研究成果: Review article同行評審

39 引文 斯高帕斯(Scopus)


The piezoelectric, phase structure and ferroelectric properties of lead-free Na0.5K0.5Nb1-xSbxO 3 piezoelectric ceramics were systematically investigated. (Na 0.5K0.5)Nb1-xSbxO3 ceramics were synthesized using the conventional solid-state reaction method. The effect of B-site Sb5+ substitution for Nb5+ on the structural characteristics and piezoelectric properties of samples was determined. According to XRD patterns, the phase gradually changes from tetragonal to orthorhombic with increasing Sb content. At x = 0.03, the tetragonal and orthorhombic phases coexist and relatively high piezoelectric properties were obtained. The relatively high Qm value obtained after substitution with Sb5+ ions might be due to the increased electronegativity and decreased ionic radius at the morphotropic phase boundary (MPB) at x = 0.03. However, the Qm value decreases with further Sb addition. Relatively high piezoelectric properties at x = 0.03 of kp = 0.42, kt = 0.48, εr = 446, Qm = 143, tan δ = 2.3%, and density = 4.31 g/cm3, d33 = 123 pC/N, were obtained.

頁(從 - 到)2061-2068
期刊Ceramics International
出版狀態Published - 2011 九月

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Process Chemistry and Technology
  • Surfaces, Coatings and Films
  • Materials Chemistry

指紋 深入研究「Sb doping effects on the piezoelectric and ferroelectric characteristics of lead-free Na<sub>0.5</sub>K<sub>0.5</sub>Nb<sub>1-x</sub> Sb<sub>x</sub>O <sub>3</sub> piezoelectric ceramics」主題。共同形成了獨特的指紋。