Selective and fast recovery of neodymium from seawater by magnetic iron oxide Fe 3 O 4

Yao Jen Tu, Sheng Chung Lo, Chen-Feng You

研究成果: Article

21 引文 斯高帕斯(Scopus)

摘要

Neodymium (Nd) is a key element that widely applied in high-tech industries; therefore, to recover it efficiently from aqueous solutions is rather important. This work examines the recovery of spiked Nd from seawater media by magnetic iron oxide (Fe 3 O 4 ). A rapid increase of Nd recovery from 0.04 to 22.27mgg -1 was observed when the solution pH adjusted from 1.98 to 8.22 at 298K. A maxima Nd adsorption capacity was estimated to be 24.88mgg -1 at 308K and 8.22 pH. A negative change in standard free energy (δG°=-5.87, -6.69, -7.68kJmol -1 at 288, 298, and 308K, respectively) suggests that Nd adsorption is spontaneous. The positive δH° value (2.42kJmol -1 ) supports its endothermic nature of the adsorption and agrees with the observed enhanced Nd adsorption at high temperatures. Besides, the positive δS° (10.84Jmol -1 K -1 ) displays that the randomness increase at the solid-solution interface during Nd adsorption. More importantly, we observed that the Nd adsorption only decreased slightly while the NaCl ionic strength increased from 0.001 to 1.0N, implying the involvement of inner-sphere mechanism. These data indicated that the adsorbent of ferrite has a great potential in selective and fast recovery of spiked Nd from seawater matrix.

原文English
頁(從 - 到)966-972
頁數7
期刊Chemical Engineering Journal
262
DOIs
出版狀態Published - 2015 二月 5

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Environmental Chemistry
  • Chemical Engineering(all)
  • Industrial and Manufacturing Engineering

指紋 深入研究「Selective and fast recovery of neodymium from seawater by magnetic iron oxide Fe <sub>3</sub> O <sub>4</sub>」主題。共同形成了獨特的指紋。

  • 引用此