Selective leaching process for the recovery of copper and zinc oxide from copper-containing dust

Jun Yi Wu, Fang Chih Chang, H. Paul Wang, Ming Jer Tsai, Chun Han Ko, Chih Cheng Chen

研究成果: Article同行評審

18 引文 斯高帕斯(Scopus)


The purpose of this study was to develop a resource recovery procedure for recovering copper and zinc from dust produced by copper smelting furnaces during the manufacturing of copper-alloy wires. The concentrations of copper in copper-containing dust do not meet the regulation standards defined by the Taiwan Environmental Protection Administration; therefore, such waste is classified as hazardous. In this study, the percentages of zinc and copper in the dust samples were approximately 38.4% and 2.6%, respectively. To reduce environmental damage and recover metal resources for industrial reuse, acid leaching was used to recover metals from these inorganic wastes. In the first stage, 2 N of sulphuric acid was used to leach the dust, with pH values controlled at 2.0-3.0, and a solid-to-liquid ratio of 1:10. The results indicated that zinc extraction efficiency was higher than 95%. A selective acid leaching process was then used to recover the copper content of the residue after filtration. In the second stage, an additional 1 N of sulphuric acid was added to the suspension in the selective leaching process, and the pH value was controlled at 1.5-2.0. The reagent sodium hydroxide (2 N) was used as leachate at a pH greater than 7. A zinc hydroxide compound formed during the process and was recovered after drying. The yields for zinc and copper were 86.9-93.5% and 97.0-98.9%, respectively.

頁(從 - 到)2952-2958
期刊Environmental Technology (United Kingdom)
出版狀態Published - 2015 12月 2

All Science Journal Classification (ASJC) codes

  • 環境化學
  • 水科學與技術
  • 廢物管理和處置


深入研究「Selective leaching process for the recovery of copper and zinc oxide from copper-containing dust」主題。共同形成了獨特的指紋。