Simultaneous control of elemental mercury/sulfur dioxide/nitrogen monoxide from coal-fired flue gases with metal oxide-impregnated activated carbon

Chun Hsiang Chiu, Hong Ping Lin, Tien Ho Kuo, Shiao Shing Chen, Tien Chin Chang, Kai Han Su, Hsing Cheng Hsi

研究成果: Article

12 引文 斯高帕斯(Scopus)

摘要

This research investigated the effects of transition metal oxide impregnation on the physical/chemical properties and on the multipollutant (i.e., Hg0/SO2/NO) control of a commercial coconut shell-based activated carbon. V, Mn, and Cu oxides of 5 wt% as their precursor metal hydroxides were impregnated onto the activated carbon surface. After the transition metal oxide impregnation, the surface area and pore volume of activated carbon decreased. The surface morphology of activated carbons was similar prior to and after impregnation. Mn3+/Mn4+and Cu+/Cu2+ were shown to be the major valence states presenting in the MnOx and CuOx/CAC samples, respectively. CuOx/CAC possessed the greatest Hg0 removal efficiency of approximately 54.5% under N2 condition and 98.9% under flue gas condition, respectively at 150°C. When the gas temperature increased to 350°C, the metal oxide-impregnated activated carbon still possessed appreciable Hg0 removal, especially for CuOx/CAC. The VOx/CAC had the largest SO2 removal enhancement of approximately 28.3% at 350°C. The NO removal of raw and impregnated activated carbon was very small under flue gas condition, indicating that adsorption of NO using metal oxide-impregnated activated carbon may not be a suitable route for NO control.

原文English
頁(從 - 到)2094-2103
頁數10
期刊Aerosol and Air Quality Research
15
發行號5
DOIs
出版狀態Published - 2015 十月 1

All Science Journal Classification (ASJC) codes

  • Environmental Chemistry
  • Pollution

指紋 深入研究「Simultaneous control of elemental mercury/sulfur dioxide/nitrogen monoxide from coal-fired flue gases with metal oxide-impregnated activated carbon」主題。共同形成了獨特的指紋。

  • 引用此