Sintering behavior and dielectric properties of yttria/silica-coated BaTiO3 material with Mn-Si-O glass

Jerry C.C. Lin, W. C.J. Wei, Chi-Yuen Huang

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

Sintering behavior and dielectric performance of yttria/silica-coated BaTiO3 powders (YSBT) with the addition of Mn-Si-O glass (0-0.5 wt%) were investigated. The sample made with YSBT powder of 0.35 μm average particle size was fully sintered at 1300°C in 1 h, and further lowered to 1200°C with 0.2 wt% glass addition. The average grain size and secondary phases of sintered BaTiO3 were characterized with XRD and TEM analyses. The resulted dielectric properties, dielectric constant, dielectric loss, and temperature-capacitance characteristic, have been examined in air or reduced atmosphere, and discussed corresponding to microstructural features.

原文English
頁(從 - 到)4103-4109
頁數7
期刊Journal of the American Ceramic Society
93
發行號12
DOIs
出版狀態Published - 2010 十二月 1

All Science Journal Classification (ASJC) codes

  • 陶瓷和複合材料
  • 材料化學

指紋

深入研究「Sintering behavior and dielectric properties of yttria/silica-coated BaTiO<sub>3</sub> material with Mn-Si-O glass」主題。共同形成了獨特的指紋。

引用此