SINTERING OF SYNTHETIC MICA BY A HYDROTHERMAL EQUIPMENT.

T. Hattori, J. Mohri, M. Yoshimura, S. Somiya

研究成果: Article

1 引文 (Scopus)

摘要

Green compacts of fluorphlogopite with 0, 5, and 10 wt% H//3PO//4 were evacuated in a borosilicate glass tube at 400 degree C for 1 h and sealed. Each capsule was isostatically hot-pressed. Synthetic mica with 10 wt% H//3PO//4 was sintered to a bulk density of 2. 71 Mg/m**3 under 150 MPa of water at 700 degree C for 3 h.

原文English
頁(從 - 到)131-132
頁數2
期刊Powder Metallurgy International
16
發行號3
出版狀態Published - 1984 一月 1

指紋

Borosilicate glass
Mica
Sintering
Water

All Science Journal Classification (ASJC) codes

  • Engineering(all)

引用此文

Hattori, T. ; Mohri, J. ; Yoshimura, M. ; Somiya, S. / SINTERING OF SYNTHETIC MICA BY A HYDROTHERMAL EQUIPMENT. 於: Powder Metallurgy International. 1984 ; 卷 16, 編號 3. 頁 131-132.
@article{a292c2c3ff8647178bba4488e4a74af2,
title = "SINTERING OF SYNTHETIC MICA BY A HYDROTHERMAL EQUIPMENT.",
abstract = "Green compacts of fluorphlogopite with 0, 5, and 10 wt{\%} H//3PO//4 were evacuated in a borosilicate glass tube at 400 degree C for 1 h and sealed. Each capsule was isostatically hot-pressed. Synthetic mica with 10 wt{\%} H//3PO//4 was sintered to a bulk density of 2. 71 Mg/m**3 under 150 MPa of water at 700 degree C for 3 h.",
author = "T. Hattori and J. Mohri and M. Yoshimura and S. Somiya",
year = "1984",
month = "1",
day = "1",
language = "English",
volume = "16",
pages = "131--132",
journal = "Powder Metallurgy International",
issn = "0048-5012",
number = "3",

}

Hattori, T, Mohri, J, Yoshimura, M & Somiya, S 1984, 'SINTERING OF SYNTHETIC MICA BY A HYDROTHERMAL EQUIPMENT.', Powder Metallurgy International, 卷 16, 編號 3, 頁 131-132.

SINTERING OF SYNTHETIC MICA BY A HYDROTHERMAL EQUIPMENT. / Hattori, T.; Mohri, J.; Yoshimura, M.; Somiya, S.

於: Powder Metallurgy International, 卷 16, 編號 3, 01.01.1984, p. 131-132.

研究成果: Article

TY - JOUR

T1 - SINTERING OF SYNTHETIC MICA BY A HYDROTHERMAL EQUIPMENT.

AU - Hattori, T.

AU - Mohri, J.

AU - Yoshimura, M.

AU - Somiya, S.

PY - 1984/1/1

Y1 - 1984/1/1

N2 - Green compacts of fluorphlogopite with 0, 5, and 10 wt% H//3PO//4 were evacuated in a borosilicate glass tube at 400 degree C for 1 h and sealed. Each capsule was isostatically hot-pressed. Synthetic mica with 10 wt% H//3PO//4 was sintered to a bulk density of 2. 71 Mg/m**3 under 150 MPa of water at 700 degree C for 3 h.

AB - Green compacts of fluorphlogopite with 0, 5, and 10 wt% H//3PO//4 were evacuated in a borosilicate glass tube at 400 degree C for 1 h and sealed. Each capsule was isostatically hot-pressed. Synthetic mica with 10 wt% H//3PO//4 was sintered to a bulk density of 2. 71 Mg/m**3 under 150 MPa of water at 700 degree C for 3 h.

UR - http://www.scopus.com/inward/record.url?scp=0021431135&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0021431135&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:0021431135

VL - 16

SP - 131

EP - 132

JO - Powder Metallurgy International

JF - Powder Metallurgy International

SN - 0048-5012

IS - 3

ER -