Solvothermal synthesis and tunable bandgap of Cu2(Zn1-xCox)SnS4 and Cu2(Fe1-xCox)SnS4 nanocrystals

Kai Liang Huang, Cheng Hao Huang, Wen Tai Lin, Yaw Shyan Fu, Tzung Fang Guo

研究成果: Article同行評審

16 引文 斯高帕斯(Scopus)

摘要

The tunable bandgap of Cu2(Zn1-xCox)SnS4 and Cu2(Fe1-xCox)SnS4 nanocrystals synthesized by the one-pot and hot-injection methods respectively was explored as a function of the Co concentration. The Co(CH3COO)2 precursor is superior to Co(NO3)2 and CoCl2 ones in enhancing the growth of pure and stoichiometric Cu2CoSnS4 (CCTS) nanocrystals. During synthesis of pure Cu2(Zn1-xCox)SnS4 nanocrystals at 270 °C for 48 h in the one-pot system, Cu3SnS4 forms first and then reacts with Co to form CCTS, and finally Zn incorporates into CCTS to form the Cu2(Zn1-xCox)SnS4 alloy. The structural transition from kesterite Cu2ZnSnS4 to stannite CCTS occurs in the Cu2(Zn1-xCox)SnS4 samples with the Co concentration (x) in the range of 0.3-0.6. The pure Cu2(Fe1-xCox)SnS4 nanocrystals were synthesized at 260 °C for 30 min by the hot-injection method. The direct bandgaps of Cu2(Zn1-xCox)SnS4 and Cu2(Fe1-xCox)SnS4 nanocrystals can be tuned in the ranges of 1.21-1.49 and 1.30-1.46 eV respectively, which decrease almost linearly with the Co concentration, showing that Cu2(Zn1-xCox)SnS4 and Cu2(Fe1-xCox)SnS4 nanocrystals may be well suited for application as the absorption layer in thermoelectric and photovoltaic devices.

原文English
頁(從 - 到)1015-1022
頁數8
期刊Journal of Alloys and Compounds
646
DOIs
出版狀態Published - 2015 七月 7

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

指紋 深入研究「Solvothermal synthesis and tunable bandgap of Cu<sub>2</sub>(Zn<sub>1-x</sub>Co<sub>x</sub>)SnS<sub>4</sub> and Cu<sub>2</sub>(Fe<sub>1-x</sub>Co<sub>x</sub>)SnS<sub>4</sub> nanocrystals」主題。共同形成了獨特的指紋。

引用此