Stacked WO3 nanosphere and WO3 thin film metal-semiconductors-metal ultraviolet photodetectors

研究成果: Article

6 引文 斯高帕斯(Scopus)

摘要

By integrating thin film and nanospheres, the metal-semiconductor-metal ultraviolet photodetectors (MSM-UVPDs) were fabricated by stacking tungsten oxide (WO3) nanospheres on WO3 thin film deposited on sapphire substrates. The sensing cutoff wavelength was 350 nm in the UVA range. Compared the WO3 nanosphere/WO3 thin film MSM-UVPDs with the thin-film structured WO3 MSM-UVPDs, due to the high surface-to-volume ratio of WO3 nanospheres, the photoresponsivity at a wavelength of 350 nm was improved from 20.7 mA/W to 89.2 mA/W, the noise equivalent power was improved from 2.35 × 10−10 W to 6.10 × 10−11 W, and the detectivity was improved from 1.34 × 109 cmHz1/2W−1 to 5.19 × 109 cmHz1/2W−1

原文English
頁(從 - 到)Q85-Q87
期刊ECS Journal of Solid State Science and Technology
7
發行號5
DOIs
出版狀態Published - 2018 一月

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials

指紋 深入研究「Stacked WO<sub>3</sub> nanosphere and WO<sub>3</sub> thin film metal-semiconductors-metal ultraviolet photodetectors」主題。共同形成了獨特的指紋。

  • 引用此