STEM-EELS Spectrum Imaging of an Aerosol-Deposited NASICON-Type LATP Solid Electrolyte and LCO Cathode Interface

Shunsuke Muto, Yuta Yamamoto, Miyuki Sakakura, Hong Kang Tian, Yoshitaka Tateyama, Yasutoshi Iriyama

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)


All-solid-state batteries (ASSBs) are promising candidates for application as next-generation high-power supply and storage devices in electric vehicles. ASSBs offer excellent safety and a high energy density; however, the high interfacial resistance between the positive electrode and solid electrolyte due to solid-solid contact reactions at elevated temperatures limits their applications. To address these issues, the effect of thermal annealing on the interfacial structure between a sodium super ionic conductor (NASICON)-type Li1.3Al0.3Ti1.7(PO4)3 (LATP) solid electrolyte and a LiCoO2 (LCO) cathode in an ASSB fabricated by aerosol deposition was investigated experimentally. Specifically, spectrum imaging was conducted by combining scanning transmission electron microscopy and electron energy loss spectroscopy. Metastable degraded low-density transition layers were formed between LATP and LCO in the as-deposited sample. A significant reduction in interfacial resistance was achieved after thermal annealing at 250-300 °C, which was mainly attributed to structural recovery in this temperature range. However, thermal annealing at 400 °C resulted in increased interfacial resistance due to the formation of a Co3O4-like spinel blocking layer at the LATP/LCO interface. These findings provided valuable insights into the electronic properties of the ASSB composite under investigation and were consistent with theoretical predictions of Li and O transfer between the layers due to thermal annealing.

頁(從 - 到)98-107
期刊ACS Applied Energy Materials
出版狀態Published - 2022 1月 24

All Science Journal Classification (ASJC) codes

  • 化學工程(雜項)
  • 能源工程與電力技術
  • 電化學
  • 材料化學
  • 電氣與電子工程


深入研究「STEM-EELS Spectrum Imaging of an Aerosol-Deposited NASICON-Type LATP Solid Electrolyte and LCO Cathode Interface」主題。共同形成了獨特的指紋。