Structural evolution of in situ boron-doped SiGe ultrathin film analyzed by multi-optical methods

Feng Ming Chang, Zong Zhe Wu, Yeh Chen, Ting Yu Yen, Yu Hsiang Huang, Li Yun Chong, Shiu Ko Jangjian, Fu Ying Lee, Yu Ming Chang, Kuang Yao Lo

研究成果: Article同行評審

摘要

In situ boron (B)-doped SiGe (BSG) layer is extensively used in the source (S)/(D) drain of metal-oxide-semiconductor field-effect transistors. An unexpected structural evolution occurs in BSG during metallization and activation annealing during actual fabrication, which involves a correlated interaction between B and SiGe. Herein, the complicated phenomena of the structural evolution of BSG were analyzed by 325 nm micro-Raman spectroscopy, x-ray photoelectron spectroscopy (XPS), reflective second harmonic generation (RSHG), and synchrotron x-ray diffraction (XRD). Optical inspection was integrated into these processes to establish a multi-optical method. 325 nm micro-Raman spectroscopy was used to determine variations in Si-Si, Si-Ge, and Ge-Ge bonds in BSG. XPS exhibited the binding energy evolution of Ge3d during different annealing processes at varied Ge ratios and B concentrations. RSHG revealed the polar Si-B and Ge-B bonds formed during annealing. Synchrotron XRD provided the structure and strain changes of BSG. Secondary-ion mass spectrometer profiles provided the species distribution, which was used to examine the results of multi-optical method. Furthermore, double-layered BSG (DBSG) with different B concentrations were analyzed using the multi-optical method. Results revealed that Ge aggregated in the homogeneous interface of DBSG, and that B dopants in BSG served as carrier providers that strongly influenced the BSG structure. However, BSG with excessive B concentration was unstable and increased the B content (SiB3) through metallization. For BSG with a suitable B concentration, the formation of Si-B and Ge-B bonds suppressed the diffusion of Ge from SiGe, thereby reducing the possibility of Ge loss and further B pipe-up in the heavily doped S/D region.

原文English
文章編號275702
期刊Nanotechnology
31
發行號27
DOIs
出版狀態Published - 2020 四月 17

All Science Journal Classification (ASJC) codes

  • 生物工程
  • 化學 (全部)
  • 材料科學(全部)
  • 材料力學
  • 機械工業
  • 電氣與電子工程

指紋

深入研究「Structural evolution of in situ boron-doped SiGe ultrathin film analyzed by multi-optical methods」主題。共同形成了獨特的指紋。

引用此