Structures of optical recording materials Ge2Sb 2+xTe5 studied by pulsed neutron diffraction

Shin Ichi Shamoto, Tomitsugu Taguchi, Toshiyuki Matsunaga, Noboru Yamada, Kenji Ishii, Toshiya Inami

研究成果: Conference article同行評審

1 引文 斯高帕斯(Scopus)

摘要

Metastable cubic Ge2Sb2+xTe5 compounds, which can be prepared only as thin films, have been studied by both of neutron and x-ray powder diffraction measurements. Large displacement of germanium atoms in a crystalline cubic Ge2Sb2Te5 phase is found by PDF analysis. By adding Sb, the crystalline cubic phases coexist with two types of amorphous phases, depending on the quenching temperature. One has a first sharp diffraction peak similar to the amorphous Sb at Q ∼1.1 Å-1. Another has a new peak at Q ∼0.74 Å -1. Based on our crystal structure analyses, the composition of the new amorphous phase was estimated to be about Ge7Sb 8Te10. The composition of the crystalline solid was also found to be different from the matrix, resulting in the nucleation dominated crystal growth in this system.

原文English
文章編號Q6.1
頁(從 - 到)125-130
頁數6
期刊Materials Research Society Symposium Proceedings
840
出版狀態Published - 2005
事件Neutron and X-Ray Scattering as Probes of Multiscale Phenomena - Boston, MA, United States
持續時間: 2004 11月 292004 12月 1

All Science Journal Classification (ASJC) codes

  • 材料科學(全部)
  • 凝聚態物理學
  • 材料力學
  • 機械工業

指紋

深入研究「Structures of optical recording materials Ge2Sb 2+xTe5 studied by pulsed neutron diffraction」主題。共同形成了獨特的指紋。

引用此