Superconducting film prepared from rapidly quenched amorphous materials of bi2Sr2Ca2-xCdxCu3Oy

Masahiro Yoshimura, Tae Hyun Sung, Nobuo Ishizawa

研究成果: Article同行評審

14 引文 斯高帕斯(Scopus)

摘要

The effect of Cd substitution for Ca in Bi2Sr2Ca2Cu3Oy has been studied using the rapid-quenching-after-rapid-melting technique. The zero resistivity temperature Tc(endpoint) increased and tailing of transition vanished with increased doping of Cd. The film with the composition Bi2Sr2Ca1.6Cd0.4Cu3Oy exhibited a Tc(endpoint) value of 87 K without tail. Further substitution of Cd for Ca brought about lowering in the Tc until finally no superconductivity transition was shown above 20 K, because a semiconducting phase with c0=2.5 nm formed instead of a c0=3.0 nm phase.

原文English
頁(從 - 到)L424-L426
期刊Japanese Journal of Applied Physics
28
發行號3 A
DOIs
出版狀態Published - 1989 三月

All Science Journal Classification (ASJC) codes

  • 工程 (全部)
  • 物理與天文學 (全部)

指紋

深入研究「Superconducting film prepared from rapidly quenched amorphous materials of bi<sub>2</sub>Sr<sub>2</sub>Ca<sub>2-x</sub>Cd<sub>x</sub>Cu<sub>3</sub>O<sub>y</sub>」主題。共同形成了獨特的指紋。

引用此