Surface characterization and platelet compatibility evaluation of surface-sulfonated chitosan membrane

C. W. Lin, J. C. Lin

研究成果: Article同行評審

22 引文 斯高帕斯(Scopus)

摘要

The effect of various sulfonated derivatives of chitosan on platelet activation and blood coagulation was examined. The surface properties of artificial biomaterials have been thought as the key factors which mediate the interactions between the biological environment and biomaterial itself. In this study, the sulfonation was directly performed on the chitosan membrane surface. The chitosan membrane was surface-sulfonated by reactions with sulfur-pyridine trioxide complex (SO3/pyridine) in H2O solution and N,N-sulfur-dimethylformamide trioxide complex (SO3/DMF) in DMF. Blood compatibility was evaluated by an in vitro platelet adhesion assay. The surface reaction of SO3/pyridine in aqueous acid medium yields N,O-sulfated chitosan with cationic NH3+ groups. After neutralization, this surface has been shown to induce a low degree of platelet adhesion and activation. When the surface-sulfonation is performed in an aqueous alkaline medium, although the degree of sulfonation is lower than the samples above, the N-sulfated chitosan significantly reduced the adhesion and activation of platelets. For the acidic SO3/DMF reaction system, N,O-sulfated chitosan was obtained with a high extent of sulfonation and cationic NH3+ groups. On this surface fully spread platelets and some platelet aggregates were found instead. This may be attributed to the ionic interactions between the platelets membrane surface and the cationic groups on the modified chitosan membrane.

原文English
頁(從 - 到)543-557
頁數15
期刊Journal of Biomaterials Science, Polymer Edition
12
發行號5
DOIs
出版狀態Published - 2001

All Science Journal Classification (ASJC) codes

  • Biophysics
  • Bioengineering
  • Biomaterials
  • Biomedical Engineering

指紋 深入研究「Surface characterization and platelet compatibility evaluation of surface-sulfonated chitosan membrane」主題。共同形成了獨特的指紋。

引用此