Surface characterization of the monolayer and Langmuir-Blodgett films of tetra-tert-butyl-copper phthalocyanine

Yuh Lang Lee, Yung Chang Chen, Chien Hsiang Chang, Yu Min Yang, Jer Ru Maa

研究成果: Article

30 引文 斯高帕斯(Scopus)

摘要

The relaxation and hysteresis phenomena of the tetra-tert-butyl-copper phthalocyanine (ttb-CuPc) monolayer were investigated. The monolayer was then transferred to a hydrophilic glass surface to prepare one monolayer of Langmuir-Blodgett (LB) films. The uniformity, stability and molecular arrangement of the LB films were studied by measurements of dynamic contact angle (DCA), and were compared with the information obtained by transmission electron microscopy (TEM) and atomic force microscopy (AFM). The results show that the monolayer of ttb-CuPc is generally stable. The limiting area of a molecule is smaller than those reported in the literature, which is attributed to the aggregation of ttb-CuPc molecules into multilayer domains. The advancing and receding contact angles of water on these LB films are much smaller than those on a homogeneous film prepared by vacuum deposition. The wettability analysis on the LB films suggests that ttb-Cu-Pc molecules are not arranged uniformly and continuously, and the LB film of ttb-CuPc contains a high ratio of exposed glass substrate. The surface morphology inspected by TEM and AFM shows the formation of separated domains of ttb-CuPc molecules, which is consistent with the surface condition evaluated from the surface wettability.

原文English
頁(從 - 到)278-284
頁數7
期刊Thin Solid Films
370
發行號1
DOIs
出版狀態Published - 2000 七月 17

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Metals and Alloys
  • Materials Chemistry

指紋 深入研究「Surface characterization of the monolayer and Langmuir-Blodgett films of tetra-tert-butyl-copper phthalocyanine」主題。共同形成了獨特的指紋。

  • 引用此