Surface morphology and wetting behavior of poly(α-methylstyrene) thin films prepared by vacuum deposition

Yuh-Lang Lee, Chi Hau Chen, Yu Min Yang

研究成果: Article

23 引文 斯高帕斯(Scopus)

摘要

Poly(α-methylstyrene) of various molecular weights was vacuum-deposited on different substrates including glass, gold, and silicon. The effects of substrate type, as well as the molecular weight of the polymer, on the morphology and wettability of the deposited films were investigated. The advancing and receding contact angles of water on the surfaces were measured by the method of Wilhelmy plate. Besides, the film surfaces were characterized with scanning electron microscopy and electron spectroscopy for chemical analysis.. The results show that the growth of the polymer on gold tends to be of the Stranski-Krastanov mode, in which the growth leads to a smoother geometry. On the other hand, the growth on glass and silicon shows the island mode and results in a rougher surface. The differences in diffusion coefficients and viscosities of the polymers of various molecular weights cause distinct island population and surface structure. The contact angles of water on heterogeneous films were examined, and the influence of fractional coverage was interpreted using a theoretical model.

原文English
頁(從 - 到)6980-6986
頁數7
期刊Langmuir
14
發行號24
出版狀態Published - 1998 十一月 24

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Spectroscopy
  • Electrochemistry

指紋 深入研究「Surface morphology and wetting behavior of poly(α-methylstyrene) thin films prepared by vacuum deposition」主題。共同形成了獨特的指紋。

  • 引用此