Synthesis and characterization of segmented liquid crystal poly(azoxy polyester‐co‐polyoxypropylene)

Jaine‐Ming ‐M Huang, Jen‐Feng ‐F Kuo, Chuh-Yung Chen

研究成果: Article同行評審

2 引文 斯高帕斯(Scopus)

摘要

In this study a series of a segmented copolyester, poly(4,4′‐dioxy‐2,2′‐dimethyl‐azoxybenzene dodecanedioyl) (PMABD)‐co‐polyoxypropylene 400 (POP), was prepared. The chain length of PMABD studied (n) was varied from 7.8‐18.2, and that of POP was unchanged. The intrinsic viscosity of the segmented copolyesters was 1.04‐1.30, and the number average molecular weight obtained was 2.53 × 104−3.49 × 104 g/mol. The mesophase texture and thermal properties of the segmented copolyesters were measured as functions of n. It was found that the insert of flexible POP between those liquid crystalline domains of PMABD did affect thermotropic properties of PMABD. As the n value was 9.0 and 7.8 (or 7.4 and 8.6% by weight POP) the texture appeared as cholesteric‐like oily streaks. The effect could not be attained by simply copolymerizing a mesogenic moiety with a pair of spacers of different lengths. The fluidity and domain structure of the flexible dodecanedioyl‐POP‐dodcanedioyl segments are taken into account for the obtained results. © 1995 John Wiley & Sons, Inc.

原文English
頁(從 - 到)165-173
頁數9
期刊Journal of Polymer Science Part A: Polymer Chemistry
33
發行號1
DOIs
出版狀態Published - 1995 一月 1

All Science Journal Classification (ASJC) codes

  • 聚合物和塑料
  • 有機化學
  • 材料化學

指紋

深入研究「Synthesis and characterization of segmented liquid crystal poly(azoxy polyester‐co‐polyoxypropylene)」主題。共同形成了獨特的指紋。

引用此