Synthesis, characterization, and electroluminescent performance of a novel copolyfluorene containing pendant crown ether groups

Juin Meng Yu, Yun Chen

研究成果: Article

7 引文 斯高帕斯(Scopus)

摘要

Copolyfluorene PFC containing pendant crown ether moieties was prepared by the palladium-catalyzed Suzuki coupling reaction. The photo-physical and electrochemical properties were investigated by absorption, photoluminescence (PL) spectroscopy, and cyclic voltammetry to elucidate the influence of the crown ether groups. In film state, its PL spectra (peaked at 430 and 452 nm) show noticeable redshift relative to 423 and 448 nm of poly(9,9-dihexylfluorene) (PF). Thermal annealing leads to appearance of new emission at about 520 nm which has been attributed to formation of excimer. The highest occupied molecular orbital and lowest unoccupied molecular orbital levels of PFC were estimated to be -5.68 and -2.65 eV which contributed to balanced charges injection. Double-layer electroluminescent device using PFC as emitting layer (ITO/PEDOT:PSS/PFC/Ca/Al) revealed maximum luminance (7910 cd/m2) and maximum luminance efficiency (2.3 cd/A) superior to those of PF device (860 cd/m2, 0.29 cd/A). Moreover, inserting a PFC layer between the PF emitting layer and calcium cathode led to reduced tum-on voltage (4.1 V), much lower than 7.1 and 6.6 V of the double-layer PFC and PF devices, respectively, and enhanced device performance (2800 cd/m2 and 0.53 cd/A).

原文English
頁(從 - 到)2985-2995
頁數11
期刊Journal of Polymer Science, Part A: Polymer Chemistry
47
發行號12
DOIs
出版狀態Published - 2009 六月 15

All Science Journal Classification (ASJC) codes

  • Polymers and Plastics
  • Organic Chemistry
  • Materials Chemistry

指紋 深入研究「Synthesis, characterization, and electroluminescent performance of a novel copolyfluorene containing pendant crown ether groups」主題。共同形成了獨特的指紋。

引用此