Synthesis of 3BaO·2CoO·12Fe2O3 powder using chemical coprecipitation

Hsing I. Hsiang, Ren Qian Yao

研究成果: Article同行評審

7 引文 斯高帕斯(Scopus)

摘要

The titration order effect on the 3BaO·2CoO·12Fe2O3 (Co2Z) ferrite formation mechanism is obtained using the coprecipitation method. This process is investigated using thermogravimetry (TG), differential thermal analysis (DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM) and superconducting quantum interference device (SQUID) magnetometer. It was found that Co2Z phase prepared using coprecipitation was obtained by the reaction of two previous formed BaFe12O19 (BaM) and Ba2Co2Fe12O22 (Co2Y) phases. For the sample obtained using back titration, the BaM phase was obtained directly by reacting BaCO3 and amorphous iron hydroxide with no α-Fe2O3 and BaFe2O4 formed as intermediates. However, owing to the existence of coarsened α-Fe2O3 and BaFe2O4 in the calcined sample obtained using direct titration, the crystallite size of the formed BaM for the sample obtained using direct titration was larger than that by back titration. Consequently, the reactivity of the formed BaM and Co2Y phases for the samples obtained using direct titration were lower than those by back titration due to the larger crystallite sizes, which led to the Co2Z phase formation temperature for the sample obtained by direct titration having a higher temperature than that by back titration.

原文English
頁(從 - 到)273-278
頁數6
期刊Journal of Magnetism and Magnetic Materials
307
發行號2
DOIs
出版狀態Published - 2006 十二月

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics

指紋 深入研究「Synthesis of 3BaO·2CoO·12Fe<sub>2</sub>O<sub>3</sub> powder using chemical coprecipitation」主題。共同形成了獨特的指紋。

引用此