Synthesis of diamond in high power-density microwave methane/hydrogen/oxygen plasmas at elevated substrate temperatures

Tsan Heui Chein, Jin Wei, Yonhua Tzeng

研究成果: Article同行評審

26 引文 斯高帕斯(Scopus)

摘要

Effects of elevated substrate temperatures and oxygen additive on the chemical vapor deposition of diamond are presented. High power-density microwave plasmas in a high concentration of methane diluted by hydrogen led to high diamond growth rates at elevated substrate temperatures up to around 1450°C. When methane and hydrogen were the only reactant gases and the substrate temperature was higher than 1450°C, graphitic deposits started to show up. With the addition of a small amount of oxygen (less than 2%), diamond films deposited at substrate temperatures higher than 1450°C at 30 μm h-1 were achieved. Diamond deposition at substrate temperatures exceeding 1600°C was achieved on molybdenum substrates. At such high temperatures, diamond grows well but the nucleation density was low. Raman spectra and surface morphologies of diamond films are correlated with the growth conditions.

原文English
頁(從 - 到)1686-1696
頁數11
期刊Diamond and Related Materials
8
發行號8-9
DOIs
出版狀態Published - 1999 八月

All Science Journal Classification (ASJC) codes

  • 電子、光磁材料
  • 化學 (全部)
  • 機械工業
  • 材料化學
  • 電氣與電子工程

指紋

深入研究「Synthesis of diamond in high power-density microwave methane/hydrogen/oxygen plasmas at elevated substrate temperatures」主題。共同形成了獨特的指紋。

引用此