Synthesis of nickel nanoparticles in aqueous cationic surfactant solutions

Dong Hwang Chen, Chih Hsuan Hsieh

研究成果: Article同行評審

241 引文 斯高帕斯(Scopus)

摘要

The synthesis of nickel nanoparticles by the reduction of nickel chloride with hydrazine in an aqueous solution of cationic surfactants CTAB/TC12AB was studied. It was found that an appropriate amount of NaOH, trace acetone, and an elevated temperature were necessary for the formation of pure nickel nanoparticles. Also, it was not necessary to perform the reaction under a nitrogen atmosphere. X-ray diffraction revealed the resultant particles were pure nickel crystalline with a face-centered cubic (fcc) structure. Their mean diameter was 10-36 nm, increasing with increasing nickel chloride concentration or decreasing hydrazine concentration. When the concentration ratio of hydrazine to nickel chloride was above 40, the mean diameter approached a constant value. The magnetic measurement on a typical sample with a mean diameter of 12 nm showed that the resultant nickel nanoparticles were superparamagnetic due to their extremely small size. The saturation magnetization, remanent magnetization, and coercivity were 32 emu g-1, 5.0 emu g-1, and 40 Oe, respectively. Also, the magnetization was observed to increase with decreasing temperature. All the observed magnetic properties essentially reflected the nanoparticle's nature.

原文English
頁(從 - 到)2412-2415
頁數4
期刊Journal of Materials Chemistry
12
發行號8
DOIs
出版狀態Published - 2002 八月 1

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 材料化學

指紋

深入研究「Synthesis of nickel nanoparticles in aqueous cationic surfactant solutions」主題。共同形成了獨特的指紋。

引用此