The 23 K superconducting phase YPd2B2C

Y. Y. Sun, I. Rusakova, R. L. Meng, Y. Cao, P. Gautier-Picard, C. W. Chu

研究成果: Article同行評審

35 引文 斯高帕斯(Scopus)

摘要

We have carried out a systematic structural, electric, and magnetic study on YPdBC samples with different compositions with emphasis on the as-cast and annealed YPd5B3C0.3 which was first reported to superconduct at ∼ 23 K by Cava et al. We found that the tetragonal body-centered YPd2B2C with lattice parameters a=3.71 A ̊ and c=10.81 A ̊ is the phase responsible for the 23 K superconductivity and that YPd2B2C is metastable, which is consistent with the suggestion made by Cava et al. [1]: it is not stable at high temperatures nor stabilizable by Ni doping, although its isostructural compound, YNi2B2C, exists. Two new phases with Y:Pd ratios of 1:7 and 2:3, respectively, have also bee detected.

原文English
頁(從 - 到)435-442
頁數8
期刊Physica C: Superconductivity and its applications
230
發行號3-4
DOIs
出版狀態Published - 1994 9月 10

All Science Journal Classification (ASJC) codes

  • 電子、光磁材料
  • 凝聚態物理學
  • 能源工程與電力技術
  • 電氣與電子工程

指紋

深入研究「The 23 K superconducting phase YPd2B2C」主題。共同形成了獨特的指紋。

引用此