The addition of Al 2O 3 in composite electrolytes consisting of polyethylene oxide and polytetramethylene glycol-based waterborne polyurethane

M. S. Wu, Ten-Chin Wen

研究成果: Article

摘要

Composite electrolytes (CEs) containing polyethylene oxide (PEO), polytetramethylene glycol based waterborne polyurethane (WPU (PTMG)), LiClO 4/propylene carbonate (PC), and aluminum oxide (Al 2O 3) were prepared by blending. The influences of the addition of Al 2O 3 in CEs were investigated using the following methods. Differential scanning calorimetry (DSC) and polarizing microscopy (PM) were employed for material characterization. The swollen weight of CEs was measured to appraise the maximum tolerated intake. Alternating current (AC) impedance was employed to obtain the ionic conductivity. Furthermore, Li/CEs/Li-CoO 2 laminated cells were assembled to measure open-circuit voltages (V oc) for the application evaluation. Accordingly, the CE consisting of 20% PEO, 20% WPU (PTMG), 10% Al 2O 3, and 50% LiClO 4/PC was found to have the best performance for all the investigated characteristics.

原文English
頁(從 - 到)47-56
頁數10
期刊Journal of the Chinese Institute of Chemical Engineers
32
發行號1
出版狀態Published - 2001 一月

指紋

Polyurethanes
Polyethylene oxides
Glycols
Electrolytes
Composite materials
Propylene
Carbonates
Aluminum Oxide
Open circuit voltage
Ionic conductivity
Differential scanning calorimetry
Microscopic examination
polytetramethylene glycol
Aluminum
Oxides

All Science Journal Classification (ASJC) codes

  • Chemical Engineering(all)

引用此文

@article{2dbab81292f44bd1b9920763c50ba1bb,
title = "The addition of Al 2O 3 in composite electrolytes consisting of polyethylene oxide and polytetramethylene glycol-based waterborne polyurethane",
abstract = "Composite electrolytes (CEs) containing polyethylene oxide (PEO), polytetramethylene glycol based waterborne polyurethane (WPU (PTMG)), LiClO 4/propylene carbonate (PC), and aluminum oxide (Al 2O 3) were prepared by blending. The influences of the addition of Al 2O 3 in CEs were investigated using the following methods. Differential scanning calorimetry (DSC) and polarizing microscopy (PM) were employed for material characterization. The swollen weight of CEs was measured to appraise the maximum tolerated intake. Alternating current (AC) impedance was employed to obtain the ionic conductivity. Furthermore, Li/CEs/Li-CoO 2 laminated cells were assembled to measure open-circuit voltages (V oc) for the application evaluation. Accordingly, the CE consisting of 20{\%} PEO, 20{\%} WPU (PTMG), 10{\%} Al 2O 3, and 50{\%} LiClO 4/PC was found to have the best performance for all the investigated characteristics.",
author = "Wu, {M. S.} and Ten-Chin Wen",
year = "2001",
month = "1",
language = "English",
volume = "32",
pages = "47--56",
journal = "Journal of the Taiwan Institute of Chemical Engineers",
issn = "1876-1070",
publisher = "Taiwan Institute of Chemical Engineers",
number = "1",

}

TY - JOUR

T1 - The addition of Al 2O 3 in composite electrolytes consisting of polyethylene oxide and polytetramethylene glycol-based waterborne polyurethane

AU - Wu, M. S.

AU - Wen, Ten-Chin

PY - 2001/1

Y1 - 2001/1

N2 - Composite electrolytes (CEs) containing polyethylene oxide (PEO), polytetramethylene glycol based waterborne polyurethane (WPU (PTMG)), LiClO 4/propylene carbonate (PC), and aluminum oxide (Al 2O 3) were prepared by blending. The influences of the addition of Al 2O 3 in CEs were investigated using the following methods. Differential scanning calorimetry (DSC) and polarizing microscopy (PM) were employed for material characterization. The swollen weight of CEs was measured to appraise the maximum tolerated intake. Alternating current (AC) impedance was employed to obtain the ionic conductivity. Furthermore, Li/CEs/Li-CoO 2 laminated cells were assembled to measure open-circuit voltages (V oc) for the application evaluation. Accordingly, the CE consisting of 20% PEO, 20% WPU (PTMG), 10% Al 2O 3, and 50% LiClO 4/PC was found to have the best performance for all the investigated characteristics.

AB - Composite electrolytes (CEs) containing polyethylene oxide (PEO), polytetramethylene glycol based waterborne polyurethane (WPU (PTMG)), LiClO 4/propylene carbonate (PC), and aluminum oxide (Al 2O 3) were prepared by blending. The influences of the addition of Al 2O 3 in CEs were investigated using the following methods. Differential scanning calorimetry (DSC) and polarizing microscopy (PM) were employed for material characterization. The swollen weight of CEs was measured to appraise the maximum tolerated intake. Alternating current (AC) impedance was employed to obtain the ionic conductivity. Furthermore, Li/CEs/Li-CoO 2 laminated cells were assembled to measure open-circuit voltages (V oc) for the application evaluation. Accordingly, the CE consisting of 20% PEO, 20% WPU (PTMG), 10% Al 2O 3, and 50% LiClO 4/PC was found to have the best performance for all the investigated characteristics.

UR - http://www.scopus.com/inward/record.url?scp=0035053047&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0035053047&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:0035053047

VL - 32

SP - 47

EP - 56

JO - Journal of the Taiwan Institute of Chemical Engineers

JF - Journal of the Taiwan Institute of Chemical Engineers

SN - 1876-1070

IS - 1

ER -