The diminishing of crystal structure of Sn9Zn alloy due to electrical current stressing

Jian Yang He, Kwang Lung Lin, Albert T. Wu

研究成果: Article同行評審

22 引文 斯高帕斯(Scopus)

摘要

The variations in the crystal structure of Sn9Zn alloy due to electrical current stressing were investigated with in situ synchrotron XRD analysis. The XRD (X-ray Diffraction) orientation peaks of both Sn and Zn crystals diminished rapidly upon current stressing. The behavior of peak diminishing indicated the electrodisruption of the crystal structure. The electrodisruption was correlated logarithmically to the strain, estimated from the XRD peak shift, as induced by current stressing. The peak diminishing of the Zn crystal was also ascribed to the electrodissolution of Zn in the Sn matrix as revealed by SEM image.

原文English
頁(從 - 到)372-377
頁數6
期刊Journal of Alloys and Compounds
619
DOIs
出版狀態Published - 2015 1月 15

All Science Journal Classification (ASJC) codes

  • 材料力學
  • 機械工業
  • 金屬和合金
  • 材料化學

指紋

深入研究「The diminishing of crystal structure of Sn9Zn alloy due to electrical current stressing」主題。共同形成了獨特的指紋。

引用此