The effect of matrix phase morphology on the structure of Ag–Cu–Pd dispersed phase dental amalgam

F. MANTE, E. H. GREENER, J. GILBERT, J. H.CHERN LIN

研究成果: Article同行評審

3 引文 斯高帕斯(Scopus)

摘要

summary The effect of an Ag–Cu–Pd dispersant alloy on the structure of amalgams fabricated with two different particle types of low‐copper amalgam matrices was investigated. In amalgams L and L (0), a low‐copper lathe‐cut amalgam Aristalloy® was used as the matrix. In amalgams S and S(0), the matrix used was Spheralloy®, a low‐copper spherical amalgam. X‐ray diffraction was used to analyse the relative content of the phases in the amalgams. The presence of Pd in the dispersant of amalgams L and S resulted in a decrease in the amount of η′(Cu6Sn5) and an increase in the amount of unreacted particles when compared to the controls L(0) and S(0). Amalgams fabricated with a spherical alloy matrix (S and S(0)) showed a greater effect than amalgams fabricated with a lathe‐cut matrix alloy (L and L(0)).

原文English
頁(從 - 到)711-715
頁數5
期刊Journal of Oral Rehabilitation
22
發行號9
DOIs
出版狀態Published - 1995 九月

All Science Journal Classification (ASJC) codes

  • 牙科 (全部)

指紋

深入研究「The effect of matrix phase morphology on the structure of Ag–Cu–Pd dispersed phase dental amalgam」主題。共同形成了獨特的指紋。

引用此