The effect of yield stress on the initiation of fatigue crack occurred from a round hole

Chung-Hung Lin, G. S. Lin, C. S. Lee

研究成果: Conference contribution

摘要

When a specimen with a round hole is subjected to cyclic loads, the maximum local stress right beside the round hole, where has a higher stress concentration factor, would exceed yield stress easily and induce plastic deformation. In this way, the actual stress range act on this region is different from the nominal stress range, and is more appropriate for the prediction of initiation of fatigue crack. Nevertheless if a specimen has lower yield stress, the actual stress range becomes smaller, which might lead to a longer life of fatigue cracks initiation. To verify the effect of lower yield stress on the fatigue cracks initiation, finite element analysis and fatigue tests were carried out by using aluminum alloy A5083-O plate specimens. To show the effectiveness of yield stress, three kinds of specimen with the same shape but with different yield stress and Young's modulus were designed. In finite element calculations the two sets of mechanical properties were used separately to obtain the actual stress range. Although the S-N curves do not show significant differences but the lower yield stress specimen has longer initial life than that of the higher yield stress. Finally, by adopting the actual stress range obtained from finite element calculations and S-N curve, estimation on the fatigue initial life occurred in a round hole is achieved.

原文English
主出版物標題Proceedings of the International Offshore and Polar Engineering Conference
頁面420-425
頁數6
4
出版狀態Published - 2001
事件11th (2001) International Offshore and Polar Engineering Conference - Stavanger, Norway
持續時間: 2001 六月 172001 六月 22

Other

Other11th (2001) International Offshore and Polar Engineering Conference
國家Norway
城市Stavanger
期間01-06-1701-06-22

    指紋

All Science Journal Classification (ASJC) codes

  • Energy Engineering and Power Technology
  • Ocean Engineering
  • Mechanical Engineering

引用此

Lin, C-H., Lin, G. S., & Lee, C. S. (2001). The effect of yield stress on the initiation of fatigue crack occurred from a round hole. 於 Proceedings of the International Offshore and Polar Engineering Conference (卷 4, 頁 420-425)