The effects of TiAl interlayer on PVD TiAlN films

Ding Fwu Lii, Jow Lay Huang, Ming Hung Lin

研究成果: Article同行評審

24 引文 斯高帕斯(Scopus)

摘要

TiAlN films with a TiAl interlayer were deposited on high-speed steel through a reactive sputtering process. A semi-coherent interface was observed between TiAl and TiAlN. Owing to the diffusion of nitrogen, a good bonding had formed between these layers. The TiAl interlayer substantially increased the adhesive strength of TiAlN films and, therefore, significantly affected the wear behavior. In addition, TiAlN films with a 1 μn TiAl interlayer exhibited the highest wear resistance.

原文English
頁(從 - 到)197-202
頁數6
期刊Surface and Coatings Technology
99
發行號1-2
DOIs
出版狀態Published - 1998 二月 5