The growth, structure and magnetic and dielectric properties of Ba 6Fe0.90Nb9.10O30 and K 4Fe1.56Nb6.44O21.4 single crystals

Jean Kuo Tai, You Yun Li, Xiaoding Qi

研究成果: Conference article同行評審

摘要

Single crystals of Ba6Fe0.90Nb9.10O 30 and K4 (Fe1.56Nb6.44)O 21.4, were grown from high temperature solution at 1380 °C and 1150 °C, respectively, by the spontaneous nucleation method. Single-crystal X-ray diffraction confirmed that Ba6Fe0.90Nb 9.10O30 belonged to the tetragonal tungsten-bronze (TTB) structure, with the space group P4/mbm (No. 127) and the lattice parameters a = 12.5895(3) and c = 3.98910(10) Å. In contrast, K4Fe 1.56Nb6.44O21.4 did not crystallize in the TTB structure and had a orthorhombic lattice instead, of which the space group was Pnma (No. 62) and the lattice parameters were a = 6.5371(6), b = 3.8212(3), and c = 18.6967(16) Å. Crystal structure analysis showed that the centers of the anion polyhedra in both crystals had distorted from the sites of the cations. The estimation from the empirical equations showed that Ba6Fe 0.90Nb9.10O30 was ferroelectric below room temperature, whereas the ferroelectric transition temperature for K 4Fe1.56Nb6.44O21.4 was as high as 820 °C. Preliminary magnetic characterization suggested that Ba 6Fe0.90Nb9.10O30 was likely to be antiferromagnetic at low temperature, while K4Fe 1.56Nb6.44O21.4 was probably paramagnetic down to 10 K.

原文English
頁(從 - 到)446-454
頁數9
期刊Procedia Engineering
36
DOIs
出版狀態Published - 2012
事件2011 IUMRS International Conference in Asia, ICA 2011 - Taipei, Taiwan
持續時間: 2011 九月 192011 九月 22

All Science Journal Classification (ASJC) codes

  • 工程 (全部)

指紋

深入研究「The growth, structure and magnetic and dielectric properties of Ba <sub>6</sub>Fe<sub>0.90</sub>Nb<sub>9.10</sub>O<sub>30</sub> and K <sub>4</sub>Fe<sub>1.56</sub>Nb<sub>6.44</sub>O<sub>21.4</sub> single crystals」主題。共同形成了獨特的指紋。

引用此