The influence of Ni nanoparticles and Ni (II) on the growth of Ag dendrites immobilized on the chelating copolymer membrane

Wei Ming Cheng, Cheng Chien Wang, Chuh Yung Chen

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

Preparation of Ag dendrites on the surface of chelating copolymer membranes (PBAGI), which was synthesized by using the soap-free emulsion copolymerization of n-butylacrylate (BA) and acrylonitrile (AN), as well as 2-methacrylic acid 3-(bis-carboxymethylamino)-2-hydroxy-propyl ester (GMA-IDA) that was used as a chelating group, is presented in this study. The characteristics of polymer membranes were investigated by Fourier transform infrared (FTIR) spectroscopy and elementary analysis (EA). The weight fraction of GMA-IDA in the polymer was 4.2 wt% as revealed by elemental analysis. The chelating group, -N(CH 2COO -Na +) 2 on the polymer was used to coordinate different amounts of Ni(II), controlled by different chelating times and subsequently reduced to Ni nanoparticles, as templates for growing Ag nanocrystals from 1.67 wt% AgNO 3 aqueous solution with 55.7 ppm poly(vinyl pyrrolidone) (PVP) added. In addition, the effect of Ni 2+ concentration on the growth of the Ag dendrites was studied. Crystallinity and morphology of Ag dendrites were examined with X-ray diffraction (XRD) and scanning electronic microscopy (SEM), respectively. Amount of Ag dendrites increased with the increasing of Ni nanoparticles on the PBAGI membrane or the dose of Ni 2+ present in the aqueous solution. Notable, under higher amount of Ni nanoparticles (over 200 mmol Ni 2+/g PBAGI membrane), Ag dendrites could be successful grown on the membrane. However, higher dose of Ni 2+ (over 41.3 ppm) might inhibit the growth of Ag dendrites.

原文English
頁(從 - 到)76-84
頁數9
期刊Materials Chemistry and Physics
137
發行號1
DOIs
出版狀態Published - 2012 十一月 15

All Science Journal Classification (ASJC) codes

  • 材料科學(全部)
  • 凝聚態物理學

指紋

深入研究「The influence of Ni nanoparticles and Ni (II) on the growth of Ag dendrites immobilized on the chelating copolymer membrane」主題。共同形成了獨特的指紋。

引用此