The influence of residual stress on the shear strength between the bone and plasma-sprayed hydroxyapatite coating

Yung Chin Yang, Chyun Yu Yang

研究成果: Article同行評審

8 引文 斯高帕斯(Scopus)

摘要

Plasma-sprayed HA coating (HAC) 50 and 200 μm thick on Ti6Al4V cylinders was transcortically implanted in the femora of canines. Push-out testing of implant-bone interfaces showed that the HAC coating exhibited higher shear strength at 50 μm coating than 200 μm one. The plasma-sprayed HACs were exhibited compressive residual stresses and the thicker HAC exhibited higher residual stress than that of the thinner HAC. Due to the structure for 50 and 200 μm implants were the same, meaning similar cohesive strength of the lamellar splats. And, there was no difference in the physiological environment; hence the difference of the shear strength for the 50 and 200 μm-HAC implants could best be attributed to the compressive residual stress existed in the HA coating.

原文English
頁(從 - 到)1051-1060
頁數10
期刊Journal of Materials Science: Materials in Medicine
19
發行號3
DOIs
出版狀態Published - 2008 三月 1

All Science Journal Classification (ASJC) codes

  • 生物物理學
  • 生物工程
  • 生物材料
  • 生物醫學工程

指紋

深入研究「The influence of residual stress on the shear strength between the bone and plasma-sprayed hydroxyapatite coating」主題。共同形成了獨特的指紋。

引用此