The multi-mechanisms and interlayer configurations of metoprolol uptake on montmorillonite

Zhaohui Li, Po Hsiang Chang, Wei Teh Jiang, Jiin Shuh Jean

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

This study assessed the mechanisms using montmorillonite (MMT) for the uptake and removal of a β-blocker metoprolol (MTP) from aqueous solution. Uptake of MTP was fast and equilibrium could be reached in 15 min and 4 h under initial MTP tartrate concentrations of 800 and 4000 mg/L, respectively. The MTP uptake capacity was as high as 412 mg/g (corresponding to 1544 mmol/kg), suggesting that MMT was a good candidate for β-blocker removal. Equilibrium solution pH and ionic strength had strong influence on MTP uptake on MMT and MTP uptake was reduced under high pH and high ionic strength conditions. Desorption of exchangeable cations matched well with the amount of MTP uptake at low loading levels, suggesting cation exchange being responsible for the uptake of MTP. At higher MTP uptake levels, significant expansion of d001 spacing was observed, confirming extensive intercalation and changes in interlayer configuration of MTP. The decomposition temperature of MTP intercalated into the MMT increased in comparison to that of crystalline MTP as revealed by thermogravimetric analyses. Band shift in FTIR analyses indicated that hydrogen bonding besides cation exchange and ion-dipole interaction was responsible for the high MTP loading levels.

原文English
頁(從 - 到)325-333
頁數9
期刊Chemical Engineering Journal
360
DOIs
出版狀態Published - 2019 三月 15

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Environmental Chemistry
  • Chemical Engineering(all)
  • Industrial and Manufacturing Engineering

指紋 深入研究「The multi-mechanisms and interlayer configurations of metoprolol uptake on montmorillonite」主題。共同形成了獨特的指紋。

引用此