The shear strength and fracture behavior of Sn-Ag-xSb solder joints with Au/Ni-P/Cu UBM

Hwa Teng Lee, Shuen Yuan Hu, Ting Fu Hong, Yin Fa Chen

研究成果: Article同行評審

30 引文 斯高帕斯(Scopus)

摘要

This study investigates the effects of Sb addition on the shear strength and fracture behavior of Sn-Ag-based solders with Au/Ni-P/Cu underbump metallization (UBM) substrates. Sn-3Ag-xSb ternary alloy solder joints were prepared by adding 0 wt.% to 10 wt.% Sb to a Sn-3.5Ag alloy and joining them with Au/Ni-P/Cu UBM substrates. The solder joints were isothermally stored at 150°C for up to 625 h to study their microstructure and interfacial reaction with the UBM. Single-lap shear tests were conducted to evaluate the mechanical properties, thermal resistance, and failure behavior. The results show that UBM effectively suppressed intermetallic compound (IMC) formation and growth during isothermal storage. The Sb addition helped to refine the Ag 3Sn compounds, further improving the shear strength and thermal resistance of the solders. The fracture behavior evolved from solder mode toward the mixed mode and finally to the IMC mode with increasing added Sb and isothermal storage time. However, SnSb compounds were found in the solder with 10 wt.% Sb; they may cause mechanical degradation of the solder after long-term isothermal storage.

原文English
頁(從 - 到)867-873
頁數7
期刊Journal of Electronic Materials
37
發行號6
DOIs
出版狀態Published - 2008 六月

All Science Journal Classification (ASJC) codes

  • 電子、光磁材料
  • 凝聚態物理學
  • 電氣與電子工程
  • 材料化學

指紋

深入研究「The shear strength and fracture behavior of Sn-Ag-xSb solder joints with Au/Ni-P/Cu UBM」主題。共同形成了獨特的指紋。

引用此