Thermal Expansion Anisotropy and Acoustic Emission of NaZr2P3O12 Family Ceramics

Varanasi Srikanth, Eleswarapu C. Subbarao, Dinesh K. Agrawal, Chi‐Yuen ‐Y Huang, Rustum Roy, Gutti V. Rao

研究成果: Article

45 引文 斯高帕斯(Scopus)

摘要

Most members of the NaZr2P3O12 (NZP) family possess low, near zero, overall thermal expansion coefficients. However, they also exhibit anisotropy of axial thermal expansion. Some compounds have opposite anisotropy; for example, the a parameter of CaZr4P6O24 contracts on heating and that of SrZr4P6O24 expands, while the c parameter expands for the Ca compound and contracts for the Sr compound. The anisotropy of the axial thermal expansion of these materials is believed to induce microcracking. The acoustic emission method was employed here to detect microcracking in ceramics due to the axial thermal expansion anisotropy. Acoustic signals were observed during cooling of the Ca and Sr compounds from 500°C, and Na and K compounds from 600°C. On the other hand, no acoustic emission signal is detected in Ca0.5Sr0.5Zr4P6O24 ceramics, in which the lattice parameters a and c remain nearly unchanged in the temperature range of room temperature to 500°C. Thus, a direct correlation between microcracking of ceramics and their anisotropic axial thermal expansion coefficients was established by employing acoustic emission monitoring techniques.

原文English
頁(從 - 到)365-368
頁數4
期刊Journal of the American Ceramic Society
74
發行號2
DOIs
出版狀態Published - 1991 二月

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry

指紋 深入研究「Thermal Expansion Anisotropy and Acoustic Emission of NaZr<sub>2</sub>P<sub>3</sub>O<sub>12</sub> Family Ceramics」主題。共同形成了獨特的指紋。

  • 引用此