Thickening of chemical vapor deposited carbon fiber

Jyh Ming Ting, N. Z. Huang

研究成果: Article同行評審

33 引文 斯高帕斯(Scopus)

摘要

Effects of temperature and hydrocarbon concentration on the thickening of CVD carbon fiber were examined. Various concentrations of hydrocarbon, ranging from 17 to 83%, balanced by hydrogen, were used. The hydrocarbon concentration ranged from 17 to 83%. The growth temperatures were 800°C, 900°C, 1000°C, 1100°C, 1200°C, 1300°C, and 1300°C. It was found that the thickening rate peaks at temperatures near 1100 and 1200°C when 40% methane and 33% propane were used as the hydrocarbon sources, respectively. At these peak thickening rates, CVD fibers exhibit rough pitted surfaces, which are not commonly seen.

原文English
頁(從 - 到)835-839
頁數5
期刊Carbon
39
發行號6
DOIs
出版狀態Published - 2001