TiO2 derived from TiC reaction in HNO3: Investigating the origin of textural change and enhanced visible-light absorption and applications in catalysis

Dong Lin Shieh, Sin Jhang Huang, Yu Cheng Lin, Yi Shiue Lin, Jong Liang Lin, Te Fu Yeh, Hsisheng Teng

研究成果: Article同行評審

5 引文 斯高帕斯(Scopus)

摘要

This paper presents the decomposition of TiC in nitric acid aqueous solution at 70°C to form porous TiO2 (anatase) containing both N and C atoms (N,C-TiO2), with visible-light sensitive catalytic activities (λ > 400 nm). TiC is gradually dissolved in the solution and transformed into spherically shaped TiO2 nanoparticles in the initial reaction stage. As these spherical particles grow to a certain size (> ∼150 nm), aggregation occurs to form porous, irregular particles. The X-ray photoelectron study indicates that the anatase contains N and C atoms with multiple bonding states. The presence of these impurities induces significantly enhanced visible light absorption, as compared to the N- or C-doped case. This porous, N and C-containing anatase shows versatile photoactivities. Under visible light irradiation, the N,C-modified TiO2 can catalyze OH radical formation demonstrated by hydroxylation of terephthalic acid. Photocatalytic degradation of methylene blue (MB) on the N,C-modified TiO 2, an air-solid model system for self-surface cleaning, at wavelengths of 314, 366, 436 and 520 nm is investigated, and exhibits a relative efficiency ratio of 1.00:0.85:0.71:0.32 after 30 min photoirradiation. The quantum yields for visible-light wavelengths of 436 and 520 nm are roughly estimated to be 4.0 × 10-5 and 1.8 × 10-5 MB molecule per photon, respectively. H2 production from water reduction over the N,C-modified TiO2 loaded with PtOx is also demonstrated.

原文English
頁(從 - 到)237-244
頁數8
期刊Microporous and Mesoporous Materials
167
DOIs
出版狀態Published - 2013

All Science Journal Classification (ASJC) codes

  • 化學 (全部)
  • 材料科學(全部)
  • 凝聚態物理學
  • 材料力學

指紋

深入研究「TiO<sub>2</sub> derived from TiC reaction in HNO<sub>3</sub>: Investigating the origin of textural change and enhanced visible-light absorption and applications in catalysis」主題。共同形成了獨特的指紋。

引用此