Transcrystallization of polypropylene composites: nucleating ability of fibres

C. Wang, C. R. Liu

研究成果: Article

146 引文 斯高帕斯(Scopus)

摘要

Transcrystallization of polypropylene (PP) on various fibres (Kevlar, PET, carbon and PTFE fibres) was investigted using a polarized optical microscope. The nucleation rate, induction time and nucleation density at saturation were detemined at various crystallization temperatures. Results show that the inverse proportion relation betwen induction time and nucleation rate which is held valid for PTFE and carbon fibre systems is not applicable to Kevlar and PET fibre systems. This is attributed to the different types of nucleation sites resulting from the non-uniformity of surface roughness of Kevlar and PET fibres. Based on the theory of heterogeneous nucleation, the interfacial free energy difference functions Δσkevlar=3.35 ± 0.24, ΔσPET = 5.87 ± 0.54, Δσcarbon = 1.14 ± 0.25, ΔσPTFE - 0.75 ± 0.12, and Δσbulk = 1.23 ± 0.07 erg cm-2. From a thermodynamic point of view, PP transcrystallinity is most likely to take place on PTFE fibres due to the lowest value of Δσ, which is consistent with the experimental findings. Moreover, induction time, nucleation rate and nucleation density at saturation are also used to characterize quantitatively the nucleating ability of fibres. A simple mechanism, based on thermal stress-induced orientation and relaxation of polymer chains, it has been proposed to account for the nucleation of transcrystallization. The topography of the fibre surface plays an important role as well. It is suggested that the presence of small-scale grooves at the fibre surfaces will cause the concentration of thermal stresses and enhance the nucleation process.

原文English
頁(從 - 到)289-298
頁數10
期刊polymer
40
發行號2
DOIs
出版狀態Published - 1999 一月

All Science Journal Classification (ASJC) codes

  • Organic Chemistry
  • Polymers and Plastics
  • Materials Chemistry

指紋 深入研究「Transcrystallization of polypropylene composites: nucleating ability of fibres」主題。共同形成了獨特的指紋。

  • 引用此