Tribological performance of 6061 aluminum alloy/graphite materials under oil-lubricated and dry sliding conditions

Jen Fin Lin, Ying Chong Yung, Chi Yuan Tsao

研究成果: Article同行評審

14 引文 斯高帕斯(Scopus)

摘要

A thrust-on-washer adapter was used to stimulate flat-on-flat-type contacts under lubricated and dry sliding conditions. The upper specimens were made of a cast aluminum alloy, A356.0 Al, and the lower specimens were prepared by powder metallurgy. Fine graphite particles were mixed with 6061 aluminum alloy powders, by means of cold pressing and sintering to create a self-lubricating composite material by means of cold pressing and sintering. The tribological performance of the composite materials was evaluated under both dry and oil-lubricated conditions. The optimum graphite content was determined by frictional performance, Stribeck curves, the product of nominal pressure and sliding speed (PV), graphite content, and wear mechanisms. The results showed that, regardless of contact pressure, the seizure, which often occurs in aluminum, can be avoided by adding graphite. Seizure can be delayed in low-speed dry sliding contacts with high graphite content. However, either too much or no graphite in aluminum alloys increases the risk of surface seizure at higher sliding speeds. Phosphorus-based additives in engine oil fail to form a boundary film on the surface of aluminum-aluminum sliding pairs; the reduced wear is purely a result of oil lubrication.

原文English
頁(從 - 到)251-261
頁數11
期刊Tribology Transactions
41
發行號2
DOIs
出版狀態Published - 1998 1月 1

All Science Journal Classification (ASJC) codes

  • 材料力學
  • 機械工業
  • 表面和介面
  • 表面、塗料和薄膜

指紋

深入研究「Tribological performance of 6061 aluminum alloy/graphite materials under oil-lubricated and dry sliding conditions」主題。共同形成了獨特的指紋。

引用此