Tribological property and drilling application of Ti-C:H and Cr-C:H coatings on high-speed steel substrates

W. H. Kao, Y. L. Su, S. H. Yao

研究成果: Article同行評審

39 引文 斯高帕斯(Scopus)

摘要

This study investigates the tribological properties and cutting performance of Ti-DLC and Cr-DLC doped metal coatings. The tribological properties of the coatings are evaluated by testing coated disks against an AISI 1045 steel counterbody under dry conditions using an oscillating friction wear tester, and then measuring the subsequent wear depth on the coated disk, the wear width on the steel counterbody, and the friction coefficient. The cutting performance of the coatings is evaluated by using coated high-speed drills to machine stainless steel workpieces, and then measuring the resulting flank wear and hole surface roughness. The results of the wear tests show that the Ti-C:H and Ti-C:H/TiC/TiCN/TiN coatings possess excellent tribological properties, including low coefficients of friction, low wear depths, and low wear widths. Regarding the machining tests, the Ti-C:H/TiC/TiCN/TiN coating has the lowest flank wear and yields the highest hole surface quality under both dry and cutting fluid drilling conditions. The single Ti-C:H coating has excellent tribological properties, but demonstrates a relatively poorer performance in the drilling of stainless steel. Finally, the Cr-DLC coatings all exhibit a poor cutting performance under dry cutting conditions.

原文English
頁(從 - 到)604-614
頁數11
期刊Vacuum
80
發行號6
DOIs
出版狀態Published - 2006 3月 10

All Science Journal Classification (ASJC) codes

  • 儀器
  • 凝聚態物理學
  • 表面、塗料和薄膜

指紋

深入研究「Tribological property and drilling application of Ti-C:H and Cr-C:H coatings on high-speed steel substrates」主題。共同形成了獨特的指紋。

引用此