Ultra low-temperature microwave annealing for ultra-shallow junctions and P-MOS devices

Ming Han Tsai, Chi Ting Wu, Shao Yu Hu, Wen Hsi Lee

研究成果: Article同行評審


Low energy ion implantation and low-temperature microwave annealing were used in this study to fabricate ultra-shallow junctions (USJs). A two-steps modulatory microwave annealing (MWA) process was employed to recover and activate a boron (400 eV) implanted silicon wafer. In the first step, 2.4 kW high power MWA was used to regrow an amorphous layer with the crystal silicon phase and thus enhance MWA absorption. After crystal silicon regrowth, 0.6 kW low power MWA was used to activate the implanted boron. The SIMS profile shows that the junction depth @5e18 was 13.5 nm, which is able to meet the requirement of the 20 nm VLSI process. The current on/off ratio (Ion/off) of the P-MOS device is higher than 106 (VDS = -0.05 V). The device subjected to two-steps MWA at 2400 W for 300 s + 600 W for 600 s had the lowest Vth. It also had the lowest subthreshold swing (SS), which means that it was best able to control the leakage current.

頁(從 - 到)27-37
期刊International Journal of Nanotechnology
出版狀態Published - 2015

All Science Journal Classification (ASJC) codes

  • Electrical and Electronic Engineering
  • Materials Chemistry
  • Condensed Matter Physics
  • Bioengineering

指紋 深入研究「Ultra low-temperature microwave annealing for ultra-shallow junctions and P-MOS devices」主題。共同形成了獨特的指紋。