XANES evidence of molybdenum adsorption onto novel fabricated nano-magnetic CuFe2O4

Yao Jen Tu, Chen-Feng You, Chien Kuei Chang, Ting Shan Chan, Sheng Hsien Li

研究成果: Article

30 引文 斯高帕斯(Scopus)

摘要

An efficient Molybdenum (Mo) removal technology in aqueous solutions was developed for the first time using nano-magnetic CuFe2O4 manufactured from printed circuit board (PCB) industrial sludge. This nano-magnetic CuFe2O4 adsorbent displayed a nonlinear L-type isotherm that fitted well with the Langmuir isotherm, suggested limited adsorption sites and monolayer sorption on surface. The K-edge X-ray absorption near-edge structure (XANES) spectra demonstrated that Mo(VI) was the predominant oxidation species on nano-magnetic CuFe2O4 and the maximum adsorption capacity was found to be 30.58mgg-1 at pH 2.75. When pH became higher, more negative charges would occur at the surface of adsorbent and lead to more electric repulsion. Consequently, Mo adsorption was sharply reduced in alkaline condition. Importantly, these adsorbed Mo anions were replaced easily by OH- ions in NaOH solution and showed huge potential for removal/concentration of Mo in industrial wastewater, groundwater, and tap water. This unique Mo separation technique can also be potentially applied for geochemical investigation in various natural aqueous solutions.

原文English
頁(從 - 到)343-349
頁數7
期刊Chemical Engineering Journal
244
DOIs
出版狀態Published - 2014 五月 15

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Environmental Chemistry
  • Chemical Engineering(all)
  • Industrial and Manufacturing Engineering

指紋 深入研究「XANES evidence of molybdenum adsorption onto novel fabricated nano-magnetic CuFe<sub>2</sub>O<sub>4</sub>」主題。共同形成了獨特的指紋。

  • 引用此