Decoration and Characterization of Bi2S3-based Nanoparticles on Reduced Graphene Oxide

  • 張 涪亮

學生論文: Master's Thesis

摘要

As a non-toxic material and abundant resource in the face of the earth bismuth sulfide was studied extensively in many fields In this study rGO/Bi2S3 was synthesized using various methods to observe its morphology and properties The methods used to synthesized Bi2S3 are hydrothermal and solvothermal methods Both of them led to nanorod structured Bi2S3 with a very large size and heavy agglomeration In the presence of graphene oxide there are some changes in the morphology of Bi2S3 which have shorter rod size and lower agglomeration degree Parameter changes was done to see its effect on Bi2S3 and rGO/Bi2S3 morphology these parameters are precursor concentration synthesis time GO content solvents the presence of capping agent and the presence of other metal sulfide The other metal sulfide used for this experiment is silver sulfide (Ag2S) which also synthesized using hydrothermal method The combination of two metal sulfides with rGO which is rGO/Bi2S3-Ag2S was synthesized using 1-step hydrothermal and 2-step hydrothermal method From these two methods the morphology of product produced was different and has different crystal structure The photocatalytic properties of synthesized nanocomposites was observed by photodegradation of methylene blue dye under the irradiation of light from 300 W xenon lamp and also using various photocatalytic parameters From the test results the photocatalytic performance of product synthesized was not good for practical use thus this material is not suitable for photocatalyst but for other applications such as supercapacitor and electrochemical sensor
獎項日期2015 一月 29
原文English
監督員Dong-Hwang Chen (Supervisor)

引用此文

Decoration and Characterization of Bi2S3-based Nanoparticles on Reduced Graphene Oxide
涪亮, 張. (Author). 2015 一月 29

學生論文: Master's Thesis